COREWELD A430Mo

Usage Recommendations:

Ferritic steels tend to be brittle due to grain growth. The heat input should be as small as possible. Low-alloy materials should be heated from 150°C to 350°C, depending on thickness. Heat treatment after welding (hardfacing) is not necessary.