Electrode for joining and hardfacing of the parts which are subject to heavy impact and abrasion.
The deposit can be hardened which increases the resistance for abrasion.
The deposit can be mechanically shaped before hardening.
After hardening, greater abrasion resistance is obtained.
Application
Hardfacing of heavy crusher components such as crushing roll teeth, crusher gears, twin roll crusher teeth, excavator buckets, railway rails (if Mn steel).
Base material
Austenitic 14% Mn steels
Low alloyed steels
All difficult to weld steels (using appropriate technology)
Typical chemical composition %
C
0,90
Mn
13,5
Cr
3,70
Ni
3,50
Mo
0,70
Typical mechanical properties
Hardness:
220 HB (afret hardfacing)
50 HRC (after hardening)
The hardness of the overlay depends on the relevant welding conditions, the number of layers and the chemical composition of the base material.